1. Definition and harm of pores in stainless steel welded pipes

Porosity in stainless steel welded pipes is a cavity formed in the weld due to the failure of gas to escape in time during the welding process. The presence of pores will cause serious harm to the quality of stainless steel welded pipes.
First, pores will reduce the strength and toughness of the weld. The presence of pores reduces the effective bearing area of the weld, making the weld prone to breakage when subjected to external force. At the same time, the metal structure around the pores may produce stress concentration due to the presence of pores, further reducing the strength and toughness of the weld.

Secondly, pores will affect the sealing of the weld. In some occasions with high requirements for sealing, such as petrochemicals, aerospace and other fields, pores in the weld may cause medium leakage, thereby causing serious safety accidents.
Finally, pores will also affect the appearance quality of the weld. Surface pores will make the weld surface uneven, affect the appearance of the product, and reduce the market competitiveness of the product.

2. Causes of pores in stainless steel welded pipes
(I) Improper surface treatment of the parent material
If there are impurities such as oil, rust, water marks, and scale on the surface of the parent material, these impurities will decompose and produce gas during welding, thereby increasing the probability of pores in the weld.

(II) Influence of welding process parameters
Parameters such as welding current, voltage, and speed have an important influence on the formation of pores. Too slow speed and too large welding current will cause the molten pool to overheat and increase the solubility of the gas, but the gas will not have time to escape during the cooling process, and pores are easily formed; too fast speed and too small welding current will cause the molten pool temperature to be too low, the molten pool has poor fluidity, and the gas is difficult to escape.

3. Prevention measures for pores in stainless steel welded pipes
Before welding, the surface of the parent material should be thoroughly cleaned to remove impurities such as oil, rust, moisture, and scale. Reasonably select parameters such as welding current, voltage, and speed. On the premise of ensuring welding quality, try to choose a smaller welding current and voltage, and appropriately reduce the welding speed to increase the gas escape time.

Guangdong Henkel Technology Co., Ltd.
Recommended reading: Laser welding production line
Hotline: 189-4243-7326

Next News：Stainless steel Tips (2)
Prev News：Stainless steel Tips (1)
【Back to previous page】
【Home】

— Related News —

Precautions for using an inter…2020-11-14
How to achieve seamless stainl…2020-11-14
How is the stainless steel int…2020-11-14
Common Pipe Problems with Lase…2025-12-05
Application and Development of…2025-11-11
In-depth analysis and technolo…2025-11-03
Technical solution of double-r…2025-09-26
Comprehensive analysis of the …2025-08-07
From single cathode to triple …2025-07-04
Innovate heat treatment proces…2025-04-22
Stainless steel weld leveling …2025-02-24
Stainless steel welded pipe ma…2025-02-19
Welded pipeline work instructi…2025-02-17
Stainless steel welding pipe m…2025-02-08
Stainless steel pipe leveling …2025-01-14
Stainless steel pipe machine m…2025-01-03
Welding porosity: unknown weld…2024-12-18
Stainless steel pipe arc pit2024-12-06
Stainless steel corrosion main…2024-11-29
Stainless steel tube not fused…2024-11-14

九九视频在线观看免费观看,亚洲欧洲中文日产,精品久久成年人免费视频,久久久精品丁香婷婷综合,日本少妇毛多水多高潮,寂寞少妇之午夜精品一区二区,国产精品一区二区资源,中文在线中文字幕人妻诱惑

GUANGDONG HANGAO TECH CO., LTD.

Stainless steel air conditioning pipe production line

Precision Welded Pipe Production Line

Rotary Black Annealing Production Line

Induction Finished Tube Bright Annealing Production Line

Weld Bead Roller Machine

Annealing Machine

Auxiliary Equipment